دانلود رایگان مقاله لاتین متالورژی آلومینیوم از سایت الزویر


عنوان فارسی مقاله:

تجزیه و تحلیل شکست متالورژی از آلومینیوم ترک خورده 7075 بال زاویه داخلی


عنوان انگلیسی مقاله:

Metallurgical failure analysis of a cracked aluminum 7075 wing internal angle


سال انتشار : 2016



برای دانلود رایگان مقاله متالورژی آلومینیوم  اینجا کلیک نمایید.





مقدمه انگلیسی مقاله:

1. Introduction

An internal angle fitting related to center box of Airbus A-300 submitted for failure investigation, which is shown in Fig. 1. This component was a structural component of a 14-year-old commercial jetliner that had carried out approximately 19,000 flight cycles when the crack was detected through NDT implementation. This type of aircraft is mostly utilized by cargo airlines. The aircraft had been grounded for service, and specific NDT operation had been implemented according to manufacturer service bulletin which notifies all operators of A-300 to conduct this test for those aircrafts that their flight cycles exceeds 17,000 cycles [1]. NDT detected a crack between two fastener holes in a way that affect residual strength of the part. Airbus had issued a service bulletin to replace this component with a modified substitute. The location of the component in the airframe is illustrated in Fig. 2. As an independent failure investigation, metallurgical properties of the angle had been studied with tests, corresponding scientific data had been gathered, and failure causes had been clarified.



برای دانلود رایگان مقاله متالورژی آلومینیوم  اینجا کلیک نمایید.






کلمات کلیدی:

A Re-Examination of Failure Analysis and Root ... - Semantic Scholar https://pdfs.semanticscholar.org/b1fb/d2c34ca072a891eb6b60af2b4c14b95cd8f7.pdf by M Zamanzadeh - ‎2004 - ‎Cited by 11 - ‎Related articles Metallurgical Failure Analysis of A Welded Hydraulic Cylinder. Case History #4. ... aluminum-iron-zinc intermetallic layer at the steel surface. This intermetallic .... primary cause of cracking of galvanized steel in bending may be the lack of an. [PDF]Practices in Failure Analysis jpkc.fudan.edu.cn/picture/article/348/.../6bd2b7ff-89c0-4500-bdc7-38c73e9ce3a2.pd... Macroscopic examination and analysis (fracture surfaces, secondary cracks, and .... the fluid that has been in contact with the metal, or of any deposits that have ..... nm, or 2 × 10-8 m, thick) of vacuum-deposited gold or aluminum to improve ... Handbook of Case Histories in Failure Analysis, Volume 2: https://books.google.com/books?isbn=0871704951 Khlefa Alarbe Esaklul - 1993 - ‎Technology & Engineering 1*228-230 extruded aluminum alloy bar stock material, cracking during ... 2*463 compressor turbine impeller cracking, metallurgical failure analysis of, Vol. Recent Case Studies in Engineering Failure Analysis Articles - Elsevier https://www.journals.elsevier.com/case-studies-in...failure-analysis/recent-articles The failure analysis of a dissimilar weld in a heat exchanger has been ... Metallurgical failure analysis of a cracked aluminum 7075 wing internal angle. October ... [PDF]Metallurgical Failure Analysis - PDH Online www.pdhonline.com/courses/m118/m118content.pdf Introduction to Metallurgical Failure Analysis ... called corrosion resistant materials such as aluminum, stainless steels and titanium that obtain their ... SCC is the formation of cracks through the simultaneous action of stress and a corrosive ... [PDF]Analysis of Metallurgical and Mechanical Failure of a Centrifugal ... ijme.us/cd_08/PDF/134_ENG_108.pdf by N Rezamahdi - ‎Related articles Analysis of Metallurgical and Mechanical Failure of a Centrifugal. Compressor ... Fatigue cracks grew to a critical size and caused the catastrophic failure of the impeller; ... is made of low alloy steel by quenched and tempered treatment.